Astm b863 gr1 gr2 gr5 gr7 gr12 2.4mm 3.2mm titanium welding wire in coil
Titanium welding wire has excellent welding process performance, beautiful weld formation, and its welded metals
have excellent comprehensive mechanical properties.
Mainly used for welding of titanium-based alloys.
Radiographic inspection requirements for weld metal inspection: Grade Ⅰ
| Product name | Titanium welding wire |
| Standard | Astm b863 |
| Material | Pure Titanium :Gr1. GR2, GR3, GR4 Alloy Titanium :GR5, GR7 ,GR12 |
| Diameter | Spool wire:φ 0.5mm, 0.6mm, 0.8mm (with wire reel) Coil wire: φ 1.0, 1.2, 1.6, 2.0, 2.4, 3.0, 4.0, 5.0mm (no wire reel) Straight wire: φ 1.2, 1.6, 2.0, 2.4, 3.0, 4.0, 5.0, 6.0mm (plastic box packing, 1000mm in length) |
| Length | Spool wire and coil wire :according to weight Straight wire:1000mm, or as customer's request |
| Product situation | Cold rolled(Y)~Hot rolled(R)~Annealed (M)~Solid Status |
Titanium wire specifications
A. Titanium wire specifications: φ0.8-φ6.0mm
B. Spectacle titanium wire specification: φ1.0-φ6.0mm special titanium wire
C. Titanium wire specification: φ0.2-φ8.0mm special for hanging tool
Grade
TA0, TA1, TA2, TA3, TA4, TA5, TA6, TA7, TA9, TA10, TC1, TC2, TC3, TC4, TC6, TC11, GR1, GR2, GR3, GR5 Ti6AL4V ELI, Ti6AL7Nb, Ti13Nb13Zr, Ti1533
standard
GB / T, GJB, AWS, ASTM, AMS, JIS
status
Annealed state (M) Hot-worked state (R) Cold-worked state (Y) (annealed, ultrasonic flaw detection)
surface
Pickled surface bright surface
use
Military, medical, sporting goods, glasses, earrings, headwear, electroplating hangers, welding wire and other industries.
Precautions for using titanium welding wire:
(1) Construction workers and welders should wear clean white gauze gloves (no cotton gloves are allowed).
(2) It is strictly forbidden to touch and touch iron objects by hand in the treated welding area.
(3) Welding work should be performed indoors as much as possible, and the ambient wind speed should be ≤0.5m / s
to avoid being affected by the wind.
(4) When welding, short arc welding should be used as much as possible, with a small welding heat input, and the
angle between the nozzle and the weldment should be 70-80 degrees.
(5) When the butt pipe is positioned and welded, its butt gap is generally about 0.5mm.
(6) Each welding seam should be completed as much as possible. The welding seams must be connected. Before
welding,
the joints should be cleaned. The length of the welding meat overlap is 10-15mm.
(7) When welding, the welding torch should not swing left and right, and the melting end of the welding wire must
not move
out of the gas protection area.
(8) Gas should be supplied in advance when welding arc initiation. Welding torch cannot be lifted immediately when
arc is extinguished. Gas supply should be delayed until the temperature drops below 250 ℃.
(9) The distance between the gas shield and the welding torch should be short, and the gap in contact with the pipe
wall should be small. When performing butt welding of pipes, in order to meet the requirements of single-sided welding
and double-sided forming, the welding is performed in two times: one for back-sealing welding (without filler materials
when back-sealing), and the other for forming welding. In multi-layer welding, the previous bead must be completely
cooled before the next bead is welded.
(10) Welding must be completely cleaned of surface impurities such as oil, rust, and moisture.
(11) To prevent the surface temperature of the bead from excessive oxidation during welding, a tail cover must be
added to enhance the protection effect.
Production Process of titanium wire:
Titanium sponge→compacting electrodes→melting→forging→bar billets→hot rolling→cold draw→titanium wires
Surface quality: high precision, good finish, no oxidation color, no cracks, peeling, thorns, marks and inclusions. Minor
local scratches, abrasions, spots and pits that do not exceed the allowable deviation of the wire diameter are allowed.
Detailed pictures:
| Chemical composition |
| Grade | Essential component<= | Impurities <= |
| Ti | Al | Mn | V | C | O | N | H | Fe |
| ERTi-1 | Remainder | — | — | — | 0.03 | 0.03-0.10 | 0.012 | 0.005 | 0.08 |
| ERTi-2 | Remainder | — | — | — | 0.03 | 0.08-0.16 | 0.015 | 0.008 | 0.12 |
| ERTi-3 | Remainder | — | — | — | 0.03 | 0.13-0.20 | 0.02 | 0.008 | 0.16 |
| ERTi-4 | Remainder | — | — | — | 0.03 | 0.18-0.32 | 0.025 | 0.008 | 0.25 |
| ERTi-5 | Remainder | 5.5-6.75 | — | 3.5-4.5 | 0.05 | 0.12-0.20 | 0.03 | 0.015 | 0.22 |
| ERTi-23 | Remainder | 5.5-6.5 | — | 3.5-4.5 | 0.03 | 0.03-0.11 | 0.012 | 0.005 | 0.20 |